Heredity in the Microstructure and Mechanical Properties of Hot-rolled Spring Steel Wire 60Si2MnA during Heat Treatment Process
Heredity in the microstructure and mechanical properties of hot-rolled spring steel wire 60Si2MnA during heat treatment process was investigated comprehensively. The steel was isothermally transformed to obtain various hot-rolled microstructure (pearlite fineness within the range of 140-510 nm) and mechanical properties, and followed by some quenching-tempering treatment. Afterwards, microstructure was characterized by optical microscopy, scanning electron microscopy and quantitative metallography, and mechanical properties were determined by tensile test. The results indicated that the hot-rolled microstructure with a coarsen pearlite structure had been changed after reheating, to a austenite microstructure with bigger and more uneven grain size, and finally to a coarsen tempered microstructure. And the average austenite grain size and standard deviation of its distribution in quenched microstructure were observed to depend linearly on the interlamellar spacing in hot-rolled microstructure. Besides, to obtain a good combination of the final strength and plasticity, an optimum value range (190-280 nm) of the interlamellar spacing had been determined for the interlamellar spacing in hot-rolled microstructure.
展开▼