>Influence of size and distribution of W phase on strength and ductility of high strength Mg-5.1Zn-3.2Y-0.4Zr-0.4Ca alloy processed by indirect extrusion
Influence of size and distribution of W phase on strength and ductility of high strength Mg-5.1Zn-3.2Y-0.4Zr-0.4Ca alloy processed by indirect extrusion
A high strength Mg-5.1Zn-3.2Y-0.4Zr-0.4Ca(wt%) alloy containing W phase(Mg_3Y_2Zn_3) prepared by permanent mold direct-chill casting is indirectly extruded at 350?C and 400?C, respectively. The extruded alloys show bimodal grain structure consisting of fine dynamic recrystallized(DRXed) grains and unrecrystallized coarse regions containing fine W phase and β2' precipitates. The fragmented W phase particles induced by extrusion stimulate nucleation of DRXed grains, leading to the formation of fine DRXed grains, which are mainly distributed near the W particle bands along the extrusion direction. The alloy extruded at 350?C exhibits yield strength of 373 MPa, ultimate tensile strength of 403 MPa and elongation to failure of 5.1%. While the alloy extruded at 400?C shows lower yield strength of 332 MPa,ultimate tensile strength of 352 MPa and higher elongation to failure of 12%. The mechanical properties of the as-extruded alloys vary with the distribution and size of W phase. A higher fraction of DRXed grains is obtained due to the homogeneous distribution of micron-scale broken W phase particles in the alloy extruded at 400?C, which can lead to higher ductility. In addition, the nano-scale dynamic W phase precipitates distributed in the un DRXed regions are refined at lower extrusion temperature. The smaller size of nano-scale W phase precipitates leads to a higher fraction of un DRXed regions which contributes to higher strength of the alloy extruded at 350?C.
展开▼
机译:Excellent formability (成形 性), forming after high artificial aging curing (人工 时效 硬化 性), high strength, low yield ratio (降 伏 比) and high ductility (延性) and with aspects rivers sheet (雨 相 钢 sheet) manufacturing How to