Exfoliation corrosion of extruded Mg-Li-Ca alloy

摘要

Exfoliation on as-extruded Mg-1 Li-1 Ca magnesium alloy was investigated after an immersion in 3.5 wt%NaCl aqueous solution for 90, 120 and 150 days through optical microscope, digital camera, scanning electron microscope, electrochemical workstation, scanning Kalvin probe, X-ray diffraction and Fourier transform infrared spectroscope. The results demonstrated that exfoliation corrosion occurred on extruded Mg-1 Li-1 Ca alloy due to elongated microstructure parallel to surface, and delamination of lamellar structure resulted from galvanic effect and wedge effect. Skin layer with fine grains exhibited better corrosion resistance, whereas the interior with coarse grains and the intermetallic compound,Mg_2 Ca particles existing in a fibrous structure, dispersed along grain boundaries and extrusion direction in a line. Furthermore, galvanic effect between Mg_2 Ca particles and their neighboring a-Mg matrix facilitated dissolution of Mg_2 Ca particles and a-Mg matrix; wedge effect was caused by formation of corrosion products. Exfoliation corrosion of extruded Mg-Li-Ca alloys might be a synergic effect of pitting corrosion,filiform corrosion, intergranular corrosion and stress corrosion. Finally, exfoliation corrosion mechanism was proposed.