Relationship between the fatigue behavior and grain structures of an as-extruded Mg-6.2Zn-0.6Zr(in wt.)alloy

摘要

Through investigating the tension-tension fatigue behavior of an as-extruded Mg-6.2 wt.%Zn-0.6 wt.%Zr(ZK60)alloy,it revealed that the determined fatigue strength at 107 cycles was quite sensitive to the grain structure.Among them,the fine grain structure had the highest fatigue strength of 130 MPa,whereas the typical“bi-modal”grain structure had the lowest fatigue strength of 110 MPa.Failure analysis demon-strated that for the fine grain structure,fatigue cracks preferentially nucleated at grain boundaries.For the“bi-modal”and coarse grain structures,the fatigue crack initiation was dominated by the cracking along slip bands.