Interface and M^(3+)/M^(2+)Valence Dual-Engineering on Nickel Cobalt Sulfoselenide/Black Phosphorus Heterostructure for Efficient Water Splitting Electrocatalysis

摘要

The catalyst innovation that aims at noble-metal-free substitutes is one key aspect for future sustainable hydrogen energy deployment.In this paper,a nickel cobalt sulfoselenide/black phosphorus heterostructure(NiCoSe|S/BP)was fabricated to realize the highly active and durable water electrolysis through interface and valence dual-engineering.The NiCoSe|S/BP nanostructure was constructed by in-situ growing NiCo hydroxide nanosheet arrays on few-layer BP and subsequently one-step sulfoselenization by SeS2.Besides the conductive merit of BP substrate,holes in p-type BP are capable of oxidizing the Co^(2+)to high-valence and electron-accepting Co^(3+),benefiting the oxygen evolution reaction(OER).Meanwhile,Ni^(3+)/Ni^(2+)ratio in the heterostructure is reduced to maintain the electrical neutrality,which corresponds to the increased electron-donating character for boosting hydrogen evolution reaction(HER).As for HER and OER,the heterostructured NiCoSe|S/BP electrocatalyst exhibits small overpotentials of 172 and 285 mV at 10 mA cm^(-2)(η_(10))in alkaline media,respectively.And overall water splitting has been achieved at a low cell potential of 1.67 V at η_(10) with high stability.Molecular sensing and density functional theory(DFT)calculations are further proposed for understanding the rate-determine steps and enhanced catalytic mechanism.The investigation presents a deep-seated perception for the electrocatalytic performance enhancement of BP-based heterostructure.