单向压缩半固态铜合金的显微组织演变

摘要

The compression deformation experiments of semi-solid ZCuSn10 copper alloy billet prepared by SIMA (strain induced melt activation) process were carried out by using Gleeble−1500 thermo-mechanical simulator test. The experimental results show that the deformation resistance of the semisolid simples prepared by SIMA method is half of as-cast ZCuSn10 copper alloy. The liquid phase rate of semi-solid sample before and after compression is 19.4% and 8.1%, respectively. Compression test under different strain, strain rate and temperature, the liquid-solid separation phenomenon occurs in transition region of the semi-solid ZCuSn10 copper alloy sample. And liquid-solid separation occurs entirely in the central region. The greater the strain is, the less liquid content of the semi-solid copper alloy compression ZCuSn10 central part of the samples. The liquid content increases with increasing temperature, and increases with increasing strain rate.%利用Gleeble−1500热/力学模拟试验机，对采用应变诱导熔化激活法制备的ZCuSn10铜合金半固态及铸态坯料进行单向压缩实验。分析压缩变形条件对半固态ZCuSn10铜合金坯料显微组织的影响，并结合压缩后的显微组织对固液两相的流动规律进行分析。结果表明：SIMA法制备的半固态压缩试样变形抗力仅为常规铸态ZCuSn10铜合金压缩试样的一半。半固态试样压缩变形前液相率为19.4%，压缩变形后液相率为8.1%。半固态ZCuSn10铜合金在不同应变量、变形温度、应变速率下进行压缩实验，试样在过渡区域开始产生液固分离现象，并在中心区域出现液固完全分离现象。变形量越大，半固态ZCuSn10铜合金压缩试样中心部位的液相越少。随着温度的升高，半固态ZCuSn10铜合金压缩试样的端部、过渡区域、心部的液相均增加。随着应变速率的增加，半固态ZCuSn10铜合金压缩试样的过渡区域的液相增加。