High-loading Pt-alloy catalysts for boosted oxygen reduction reaction performance

摘要

To improve performance of membrane electrode assembly(MEA)at large current density region,efficient mass transfer at the cathode is desired,for which a feasible strategy is to lower catalyst layer thickness by constructing high loading Pt-alloy catalysts on carbon.But the high loading may induce unwanted par-ticle aggregation.In this work,H-PtNi/C with 33%(mass)Pt loading on carbon and monodisperse distri-bution of 3.55 nm PtNi nanoparticles,was prepared by a bimodal-pore route.In electrocatalytic oxygen reduction reaction(ORR),H-PtNi/C displays an activity inferior to the low Pt loading catalyst L-PtNi/C(13.3%(mass))in the half-cell.While in H_(2)-0_(2) MEA,H-PtNi/C delivers the peak power density of 1.51 W·cm^(-2) and the mass transfer limiting current density of 4.4 A·cm^(-2),being 21%and 16%higher than those of L-PtNi/C(1.25 W·cm^(-2),3.8 A·cm^(-2))respectively,which can be ascribed to enhanced mass trans-fer brought by the thinner catalyst layer in the former.In addition,the same method can be used to pre-pare PtFe alloy catalyst with a high-Pt loading of 36%(mass).This work may lead to a range of catalyst materials for the large current density applications,such as fuel cell vehicles.