The behavior of the reinforcement of submicron composite Al_ 2 O_ 3 p/6061Al in molten pool during laser welding was studied. It was indicated that because there were the remarkable differences in thermal physical properties between matrix and reinforcement particulate, the reinforced particulate was pushed forward during molten pool solidification by the liquid-solid interface in matrix and the reinforced particulate segregated in the weld. It resulted in noticeable degradation in properties of the welded joint. The technology methods to improve the behavior of reinforcement were also investigated. Itwas pointed out that the laser pulse frequency is the main welding parameter affecting the distributive state of reinforcement, and the theory basis was established for welding the material by laser beam.