TC4-DT钛合金线性摩擦焊接头组织和力学性能分析

摘要

针对飞机用典型的TC4-DT钛合金线性摩擦焊接头,开展组织及接头的拉伸、冲击和低周疲劳等力学性能测试.结果表明:TC4-DT钛合金线性摩擦焊接头经过700℃+保温3h的热处理后,接头的室温和高温抗拉强度达到母材的97%以上,室温和低温冲击性能略高于母材,室温低周疲劳性能与母材相当,具有良好的综合力学性能.%The Microstructure, tensile strength, impact property and low-cycle fatigue testing properties were studied for TC4-DT liner friction welded (LFW) joint of the aircraft. Test results show that an excellent properties of weld joint can be obtained after post-weld heat treatment (temperature: 700℃ , longtime: 3h). The room and high tensile strengths of TC4-DT LFW joint can reach more than 97% of TC4-DT base metals, and the impact property of the weld joint is slightly higher than the base metal, the low-cycle fatigue property is close to the TC4-DT base metals.