Hot Deformation Behavior of Sicw/AZ91 Magnesium Matrix Composite in Compression

摘要

The compressive behavior of squeeze cast SiCw/AZ91 composite in the temperature range of 423-723K and in the strain rate range of 0.001-0.25 s~(-1) was investigated. The compressive true stress-true strain curves were measured and hot deformation microstructures were observed. The strain rate sensitivity exponent (m) of the SiCw/AZ91 composite increased with the increasing of temperature. The activation energy of deformation varied over the range of test conditions examined indicated that the deformation was controlled by more than one mechanism. The reorientation of SiC whiskers in the composite was observed during compression. During the compression, dynamic recovery and dynamic recrystailization occurred in the SiCw/AZ91 composite.