摘要

Coiled tubing (CT) bending fatigue has been the subject of much research. Slickline (SL) fatigue is the subject of more recent, ongoing research. Fatigue life tracking and prediction systems are available for both CT and SL. However, these systems do not adequately include the reduction in life due to corrosion. This paper discusses the CT and SL fatigue, and presents a new approach to handling the life reduction due to corrosion.

机译：弯曲管（CT）弯曲疲劳是有多大研究的主题。 Slickline（SL）疲劳是更近期，正在进行的研究的主题。疲劳寿命跟踪和预测系统可用于CT和SL。然而，这些系统没有充分地包括由于腐蚀而降低了生命的减少。本文讨论了CT和SL疲劳，并提出了一种处理由于腐蚀引起的生命减少的新方法。

著录项

来源
《SPE/ICoTA Coiled Tubing Well Intervention Conference Exhibition》|2007年||共6页
会议地点
作者
Kenneth R. Newman;
展开▼
作者单位

展开▼
会议组织
原文格式 PDF
正文语种
中图分类石油、天然气工业;
关键词

相似文献

外文文献
中文文献
专利

1. Fatigue failure of a Slickline wire induced by corrosion pits [J] . W. Hormaza, G.M. Castro Giiiza, L.M. Mendez Moreno Engineering failure analysis . 2014,第Null期

机译：腐蚀坑引起的钢丝润滑脂疲劳失效
2. Pit to crack transition and corrosion fatigue lifetime reduction estimations by means of a short crack microstructural model [J] . Balbin J. A., Chaves V., Larrosa N. O. Corrosion science . 2021,第Mara期

机译：坑通过短裂纹微结构模型裂开转变和腐蚀疲劳寿命减少估计
3. Effect of pre-corrosion and corrosion/fatigue alternation frequency on the fatigue life of 7B04-T6 aluminum alloy [J] . Tengfei Cui, Daoxin Liu, Jian Cai, Journal of Materials Research . 2016,第24期

机译：预腐蚀和腐蚀/疲劳交替频率对7B04-T6铝合金疲劳寿命的影响
4. Measuring CT and Slickline Fatigue Life Reduction Due to Corrosion [C] . Kenneth R. Newman SPE/ICoTA Coiled Tubing Well Intervention Conference Exhibition . 2007

机译：测量腐蚀导致的CT和Slickline疲劳寿命降低
5. A lifetime-prediction approach to understanding corrosion: The corrosion-fatigue and corrosion behavior of a nickel-based superalloy and a nanocrystalline alloy. [D] . Steward, Rejanah Vernice. 2006

机译：预测腐蚀的寿命预测方法：镍基高温合金和纳米晶合金的腐蚀疲劳和腐蚀行为。
6. Effect of Pre-Corrosion Pits on Residual Fatigue Life for 42CrMo Steel [O] . Dezheng Liu, Yan Li, Xiangdong Xie, 2019

机译：预腐蚀坑对42CrMo钢残余疲劳寿命的影响
7. Study of Corrosion-Fatigue : On a method of measuring damage caused by Corrosion-Fatigue [O] . Kanetoshi IWAMOTO 1957

机译：腐蚀性疲劳研究：关于腐蚀疲劳损伤的方法
8. Corrosion Fatigue Crack Propagation in Aluminum Alloys. Part I. Effect of Cyclic Stress Wave Form on Corrosion Fatigue Crack Propagation in Al-Zn-Mg Alloys. Part II. Mechanisms of Corrosion Fatigue Crack Propagation in Al-Zn-Mg Alloys [R] . Selines, R. J., Stoltz, R. E., Pelloux, R. M. 1972

机译：铝合金腐蚀疲劳裂纹扩展。第一部分循环应力波形对al-Zn-mg合金腐蚀疲劳裂纹扩展的影响。第二部分。 al-Zn-mg合金腐蚀疲劳裂纹扩展机理

Measuring CT and Slickline Fatigue Life Reduction Due to Corrosion

摘要

著录项

引文网络

相似文献

相关主题

期刊订阅