High Performance Unalloyed Ductile Cast Iron with Multiphase Structure

摘要

An unalloyed ductile cast iron with a multiphase structure is designed by a novel austempering process. The designed austempering treatment consists of initial rapid quenching to 180°C after austenizing at 890°C for 20min, and finally austempering at 220°C for 240min. A multiphase structure comprising lenticular/needle-like prior martensite, fine needle bainitic ferrite and film retained austenite is obtained. The excellent mechanical properties, with a tensile strength of 1530MPa and an elongation of 3.1% can be achieved by controlling the matrix microstructure of 12% prior martensite, 15% retained austenite with 1.64% carbon content, and 73% bainitic ferrite. This is mainly attributed to prior marteniste which can promote refinement of multiphase colonies.