Drying Temperature Effects on Electrical and Optical Properties of poly2-methoxy-5-(2'-ethyl-hexyloxy)-1,4-phenylene vinylene (MEH-PPV) Thin Film

摘要

Temperature effects on electrical and optical properties of a representative semiconducting polymer, poly[2-methoxy-5-(2'-ethyl-hexyloxy)-1,4-phenylene vinylene] (MEH-PPV), has recently attracted much attention. The MEH-PPV thin films were deposited at different drying temperature (anneal temperature) using spin-coating technique. The spin coating technique was used to produce uniform film onto large area. The MEH-PPV was dissolved in toluene solution to exhibits different optical and electrical properties. The absorption coefficient and bandgap was measured using UV-Visible-NIR (UV-VIS-NIR). The bandgap of MEH-PPV was effect by the thickness of thin films. For electrical properties, two-point probe was used to characterize the current-voltage measurement. The current-voltage measurement shows that the MEH-PPV thin films become more conductive at high temperature. This study will provide better performance and suitable for optoelectronic device especially OLEDs applications.