Preparation of WC/Ni Flexible Cloth Coating by Vacuum Brazing

摘要

In this study, one novel WC/Ni flexible cloth coatings were prepared to enhance the abrasion and erosion resistances and meanwhile to accommodate the complicated component surfaces. Neither precipitation of WC particle nor pores or cracks were detected in the coating. The scarification extent of WC particle decreased with the increase in the WC content. With the abrasion mechanism of three body abrasive wear, the WC/Ni coating with 59.8 wt.% WC (WC/Ni-59.8 wt.%) showed the best abrasion resistance with the wear rate of 0.3% of 304 stainless steel. At 30° of impact angle, the WC/Ni-59.8 wt. % exhibited a superior erosion resistance to that of WC coating developed by high vel°City oxygen fuel (HVOF). The application potential of WC/Ni flexible cloth coating for the commercial components was testified by developing the coating on a ball valve disc.