This study aimed to enhance the properties of aluminium-silicon (Al-Si) alloys by adding zinc oxide as a reinforcing material. This study was a type of pre-experimental design called the one-shot case study, in which sample groups subjects were given treatments and then observed. The steps included melting the aluminium-silicon in a furnace at 900°C, adding a certain amount of zinc oxide (0.05%, 0.1%, or 0.2%), stirring the mixture for 1 minute, and pouring it into a permanent mould. Results showed that, among the three specimens, the specimen reinforced with 0.2% zinc oxide had the highest tensile strength of 23.9 kg/mm~2, the greatest hardness of 134.4 HV, and a flat surface with evenly distributed grains and more brittle fracture.
展开▼
机译:该研究旨在通过将氧化锌作为增强材料加入氧化锌 - 硅(Al-Si)合金的性质。该研究是一种称为单次案例研究的实验性设计,其中给予样品组受试者进行治疗,然后观察到。包括在900℃的炉中熔化铝 - 硅的步骤,加入一定量的氧化锌(0.05%,0.1%或0.2%),将混合物搅拌1分钟,并将其倒入永久模具中。结果表明,在三个标本中,用0.2%氧化锌加固的样品具有23.9 kg / mm〜2的最高抗拉强度,最大的硬度为134.4 hV,以及具有均匀分布的晶粒和更脆的碎片的平坦表面。