摘要

Kenaf fiber has a great potential to be replaced with the synthetic composite due to their advantages such as environmentally friendly and outstanding performance. However, the main issue of this natural fiber that to be used in structural composite is inconsistency of their mechanical properties. Here, the influence of the gage length on the mechanical properties of single kenaf fiber was evaluated. This fiber was tested using the Universal testing machine at a loading rate of lmm per min following ASTM D3822 standard. In this study, the different length of treated fiber including 20, 30 and 40mm were being tested. Following, Weibull probabilities analysis was used to characterize the tensile strength and Young modulus of kenaf fiber. The predicted average tensile strength from this approach is in good agreement with experimental results for the obtained parameter.