Microstructure and mechanical properties of 2.5 vol. TiBw/Ti6Al4V composites plates fabricated by hot-hydrostatic canned extrusion

摘要

Plates of 2.5 vol. % TiB whisker-reinforced Ti6Al4V titanium matrix composites (TiBw/Ti64) with network structure were successfully fabricated by hot-hydrostatic extrusion with steel cup at 1100°C. The dimensions of plates were about 150mm in length, 27mm in width and 2mm in thickness. After extrusion, the original equiaxed-network structure formed by TiB whiskers still existed, but was compressed in cross-section and stretched in longitudinal section and then the TiB whiskers were directional distribution along the extrusion direction. Furthermore, the mechanical properties results showed that the strength, hardness and ductility of the plates were significantly improved compared to as-sintered composites.