Ultrasonic Pulse Method - Influence of Internal Compressive Stress on Results of Testing Calcium Silicate Bricks

摘要

Measuring with ultrasonic pulse method is influenced by various factors, like loading in particular inner tension when material built in a construction is tested. The paper researches influence of inner tension (load) on testing of calcium silicate bricks with ultrasonic pulse method. Calcium silicate bricks were loaded with force corresponding to 0 % (unloaded test specimens), 10 %, 20 %, 50 %, 60 % of ultimate compressive strength with various content of humidity (dried samples, w=2 %, w=8 % and samples saturated with water). It was found that ultrasonic pulse velocity is not considerably influenced at load of 10% and 20% of ultimate strength of bricks. However, ultrasonic pulse velocity considerably decreases after loading at 50% and 60% of ultimate compressive strength. Most of theoretical assumptions concerning mentioned concrete stated in technical literature were confirmed, however, particular values were different because of differences between concrete and calcium silicate bricks.