The Optimal Ratio of Mixed Talc Silica and Narathiwat Clay for Cordierite - Mullite Refractories

摘要

In this paper, effects of incorporation of Narathiwat clay (NT), talc and silica on the mechanical properties of cordierite-mullite refractories were investigated. The starting raw materials were mixed in different ratios and fired at 1300 °C for 2 hours. XRD patterns of fired refectories indicated cordierite and mullite phases. The fired samples were studied the firing shrinkage, water absorption, bulk density, apparent porosity and bending strength of the cordierite-mullite refractories. The optimum condition was achieved for the composition of 20% Talc that had shrinkage: 11.78%, water absorption: 4.16%, bulk density: 2.28 g/cm~3, apparent porosity: 9.2% and bending strength: 330.82 kg/cm~2. The results thus showed that Narathiwat clay, talc and silica was a potential materials for as cordierite-mullite refractories.