Comparison of Corrosion Performance of Grade 316 and Grade 347H Stainless Steels in Molten Nitrate Salt

摘要

Stainless steel samples machined from SA-312 TP316 and SA-213 TP347H pipe were exposed to a molten nitrate salt environment at 600°C (1112°F) for up to 3000 hours in order to generate corrosion rates for use in concentrated solar power (CSP) facilities. Descaled weight loss measurements were made at 1000, 2000, and 3000 hours, with optical and scanning electron microscopy being performed on samples at the longest exposure time. The 316 and 347H alloys exhibited metal losses of 4.4 and 4.8 um respectively at 3000 hours. A linear fit to the data sets yielded annualized metal loss rates of 8.4 and 8.8 um/yr. The oxides were relatively uniform in thickness and multilayered. The inner layer consisted of a (Fe, Cr)-spinel with appreciable amounts of Mn while the outer layer was an oxide composed of only Fe. No pitting, intergranular attack, or other localized attack was found, despite the presence of a sensitized microstructure in both alloys and chloride impurity in the salt mixture. The observations presented here indicate that the two alloys perform quite comparably with respect to molten salt-induced corrosion and in that regard; either would be expected to perform satisfactorily in the intended application.