Study on the Waterproofing Properties of Cement-based Composite Thermal Insulation Materials

摘要

Polystyrene granules (EPS) for lightweight aggregate and cement for cementing material, while adding a variety of additives, were used to prepare cement-based composite thermal insulation materials by the method of vibration molding. The effects of different waterproof agent on water absorption and strength of cement-based composite thermal insulation materials were studied contrastively by adding emulsified stearic acid and emulsified composite waterproofing agent, and the related mechanisms were analyzed. Results showed that the waterproofing effect and strengthen effect of emulsified composite waterproofing agent is superior to emulsified stearic acid, when the content of emulsified stearic acid and emulsified composite waterproofing agent are 5% and 5%, respectively, the 2h, 24h water absorption of samples are 20.59%, 47.64% and 15.53%, 34.53%, the flexural and compressive strength of samples are 0.32MPa, 0.42MPa and 0.35MPa, 0.47MPa.