Effect of Annealing Temperature on the Transformation Temperature and Texture of Ni_(47)Ti_(44)Nb_9 Cold-rolled Plate

摘要

Transformation behaviors and texture of Ni_(47)Ti_(44)Nb_9 cold-rolled plates were studied by differential scanning calorimetry and X-ray diffraction test. R phase transformation does not occur in Ni_(47)Ti_(44)Nb_9 cold-rolled plate annealed at 350°C-750°C followed by quenching into the water. Martensite transformation temperature first increases and then decreases with increment of annealing temperature, and the maximum achieves at 700°C. The heat of reverse martensite transformation increases, while hardness decreases as annealing temperature increases. The major texture of cold-rolled plate is {332}<110>and spread from {332}<110>to {110}<110>. When the annealing temperature is above 600°C, the major textures are {332}<113>and {111}<112>recrystallization texture in secondary cold-rolled plate.