Effect of Composition of Cementitious Materials on Alkalinity of Pore Solution and Strength of Cement Paste

摘要

Alkalinity of the surroundings is the basis to study the MICP technology. Alkalinity of pore solution and strength of cement paste made of various cementitious materials were studied. Results show that the alkalinity of pore solution of cement paste decreased with the increase of sulpho-aluminate cement content. pH value of cement paste was about less than 10 when sulpho-aluminate cement content exceeded 75%. Incorporation of sulpho-aluminate cement decreased compressive strength of paste obviously; however, compressive strength of paste was improved when the addition of sulpho-aluminate cement was more than 75%. Addition of mineral admixtures reduced the alkalinity of pore solution of cement paste and increased its compressive strength. Compressive strength of specimens was decreased when the content of mineral admixtures increased.