Corrosion Resistance of Copper infiltrated on 0Cr18Ni9 Austenitic Stainless Steel by Plasma Surface Technology

摘要

Copper is infiltrated on 0Cr18Ni9 austenitic stainless steel surface by Double Glow Plasma technology, the surface copper content is about 3.5%, content of Cr in metal infiltration layer reaches up to 29.2%. Under the conditions of normal pressure and temperature, corrosion resistance of stainless steel samples which copper infiltrated on surface was researched in 1 mol/L NaOH solution by measurement method of electrochemical. The result shows that, corrosion resistance of copper-infiltrated stainless steel is about 1.67 times higher than untreated sample in 1 mol/L NaOH solution.