In-Situ Cold Temperature XRD of Calcium Phosphate Produced From Organic Phosphoric Acid

摘要

In this study, we synthesized calcium phosphate from an organic phosphoric acid, diethylhexyl phosphoric acid (DEHPA) and calcium hydroxide solution. The reaction involves a sol-gel process with a whitish gel formed. In-situ XRD analysis was then performed on the sample from room temperature to -140°C. At room the XRD diffractogram shows the sample as an amorphous material and as the temperature was further lowered sharp peaks begins to form indicating that the material had becomes crystalline. The peaks were identified to be that calcium hydrogen phosphate (Ca(H_2PO_4)_2) and this indicates that there is no hydroxyl group removal during the cooling process. The relative crystallinity values obtained for the different cooling temperatures show a slow exponential increase on the initial cooling of 0 to -100°C and at further cooling temperatures resulted fast and linear process. Also unlike the in-situ XRD analysis performs at high temperature no phase transformation occurred at this low temperature.