EFFECT OF POLY (LACTIC-CO-GLYCOLIC ACID) (75:25)/HYDROXYAPATITE COMPOSITE ON CHONDROCYTE CULTURE FOR TISSUE RECONSTRUCTION

摘要

PLGA (75:25)/hydroxyapatite (HA) composite films were fabricated by solvent-casting method to investigate the effect of various hydroxyapatite content ratio to the PLGA film for cellular attachment and proliferation. Mechanical property of the composite film was characterized by tensile test. The ultimate tensile strength of 10 percent HA content film was two folds higher than control group. The surface of the film was characterized by contact angle measurement. The PLGA/HA composite film was more hydrophilic than control film. In vitro chondrocyte responses to the composite films were measured by cellular attachment and proliferation test. The attached and proliferated cells were significantly higher on PLGA/HA (10 percent) composite film than control group (1.44 times higher in attachment test and 1.31 times higher for 6th-day at culture in proliferation assaying, p<0.05). Base on these finding, the PLGA/HA (10 percent) composite was effective for the cell attachment for the initial stage of cultivation and cell proliferation.