ULTRASONIC FATIGUE BEHAVIOR OF WELDED JOINTS WITH SHOT PEENING TREATMENT

摘要

In order to investigate the ultra-long life fatigue properties of welded joints, ultrasonic fatigue tests of base material and welded joints were carried out using Q345q steel in ambient air at room temperature with a stress ratio R=-1. The results showed that the fatigue strength of specimens with welded joints dropped about 60% compared with that of base steel. To improve the fatigue properties of welded joints, two groups of specimens were treated by shot peening with different degrees which produced different compressive residual stresses on sample. It was found that the shot peening treatment could improve the fatigue strength of welded joints obviously. The fatigue fracture surface was analyzed by scanning electron microscopy. The fractography showed that there were two kinds of crack initiation mechanism in the Q345q base steel, crack inition from defects on the surface for high cycle fatigue fracture and in the interior of the sample for very high cycle fatigue range. However, almost all cracks of welded joints initiated from defects caused by welding process. The facture of welded joints usually happened at the section of welded toes in the area of fusion or geometric discontinuity.