Yttria Stabilized Zirconia Nanopowders from L-FSP Technology: Structural, Dispersion, and Sintering Properties

摘要

Nanopowders of yttria stablized zirconia (2 and 8mol% Y{sub}2O{sub}3) are produce by NANOCEROX using Liquid Phase-Flame Spray Pyrolysis (L-FSP) technology. Particle size was studied using SEM and laser scattering. The primary particle size is 50-80nm with spherical shape. Particles dispersed in DI water showed agglomerates with the size of 50-150nm. Zeta potential andpH value of 0.25wt% particle in DI water system were measured. The effect of pH and dispersant on zeta potential were studied. High density (>99%) 2Y-TZP ceramics were achieved after low temperature (1200°C) air sintering. The strength was 1.70±0.03GPa. High density 8YSZ ceramics (>95%) were also prepared.