Preparation and Application of PoIy(Acrylic Acid-co-Acrylamide) on Scale and Corrosion Inhibition

摘要

This research is focused on the synthesis and the ability to inhibit scale and corrosion of poly(acrylic acid-co-acrylamide) (PAA-AM copolymers). A series of polymers were synthesized by free radical polymerization having various weight ratios of acrylic acid (AA) to acrylamide (AM). The structures of the synthesized polymers were characterized by UV-Vis Spectroscopy, FT-IR, and ~1H-NMR. The thermal stability of the polymers was analyzed by a TGA technique. The water solubility of the polymers was examined using a turbidity meter. The scale inhibition performance test was performed by titration of calcium ion with ethylene diamine tetraacetic acid (EDTA) solution. After that, the crystal structure of CaCO_3 scale from the scale inhibition test was examined using a scanning electron microscope. The efficiency of the corrosion inhibitor on low carbon steel AISI 1018 was investigated by a potentiodynamic polarization technique. The result show that PAA-AM copolymers having a 9:1 weight ratio with 45.82% at 100 ppm inhibited scale forming. The corrosion resistance of all inhibitors could be achieved when the concentration of the inhibitor was lower than 100 ppm.