Development and fabrication of PAMAM-based composite membrane module with a gutter layer of Chitosan/PAA polymer double network for CO2 separation

摘要

To improve the CO2 separation performance of a poly(amidoamine) (PAMAM) dendrimer composite membrane, a gutter layer of chitosan(CTS)/polyacrylic acid(PAA) polymer double network (DN) and its fabrication are proposed. In our previous studies, PAMAM-based composite membrane module with a gutter layer of cross-linked CTS showed high CO2 separation properties from CO2/N2 mixed gases. In this study, CTS/PAA polymer DN was used to prepare the gutter layer instead of CTS to enhance CO2 permeance and pressure durability of PAMAM-based composite membrane. A PAMAM dendrimer composite membrane module with a gutter layer of CTS/PAA polymer DN, which was prepared with a coating solution of CTS/PAA (CTS/PAA=l/2 molar ratio), showed a high permeance of 8.8 x 10~(-11) m~3 (STP) m~(-2) s~(-1) Pa~(-1) with a high CO2 separation factor of 104 at 40 °C, pressure 550 kPa with a feed gas mixture CO2/N2=5/95 (vol. /vol.).