FABRICATION OF HIGH STRENGTH AND TOUGHENED BIODEGRADABLE ELECTROSPUN FIBERS: POLY(LACTIC ACID)/BIOMAX BLENDS

摘要

The objective of this study is to prepare a toughened and strengthened electrospun fibrous biodegradable poly(lactic acid) (PLA) mat blended with Biomax, an ethylene copolymer designed to modify PLA to improve toughness properties, using electrospinning. Morphological, thermal, mechanical, and thermomechanical properties of PLA/Biomax blends were investigated. Morphological findings indicated that the electrospun PLA/Biomax fibers were uniform and smooth with an average diameter of 1.4-1.5 μm when Biomax contents below 2 % (w/v). The addition of 1 % of Biomax improved both thermal stability and mechanical properties of PLA/Biomax fibrous mats. PLA/Biomax mats with 1 % (w/v) of Biomax exhibited the maximum tensile strength of 4.6 MPa and tensile modulus of 103 MPa showing 64.3 % and 101 % improvement; as compared to neat PLA values of 2.83 MPa and 51 MPa, respectively. Furthermore, the presence of 1 % Biomax into electrospun PLA fiber mats improved the storage modulus by 107.5 % compared to PLA fiber mat (41.5 MPa). Strong and toughened PLA/Biomax biodegradable fibrous mat might be potentially suitable to be used in packaging, filtration, reinforcement of composite, etc.