Isothermal Martensite Formation at Sub-Zero Temperatures

摘要

Sub-zero treatment of steels with an M_f, below 0°C relies (partly) on a continuation of the martensite formation. The present work reports on the observation of isothermal martensite formation in the sub-zero temperature regime for two steels: AISI 1070 and AISI 52100. Samples were austenitized, quenched in oil, and thereafter investigated with vibrating sample magnetometry, which allows a quantitative assessment of the fraction of retained austenite as a function of the sub-zero temperature and time. Isothermal martensite formation was observed on interrupting the continuous cooling (5 K/min) at temperatures in the range of 80-233 K. The kinetics of isothermal martensite formation depends strongly on the temperature and can be described by Johnson-Mehl-Avrami-Kolmogorov kinetics. Isothermal experiments with dilatometry indicated the occurrence of a volume increase on isothermal holding, consistent with a continuation of the martensitic transformation. On prolonged isothermal holding, a volume reduction was observed for AISI 52100, but not for AISI 1070.