(9547)SUPPRESSION OF INTERNAL DEFECTS IN COLD DRAWING OF PURE MAGNESIUM WIRE

摘要

Pure magnesium is a material with high functionality, however, the cold drawing of this material is very difficult, that is why, until this day there are no optimal cold drawing conditions. Furthermore, cold drawing of pure magnesium wire shows a problem with internal defects that occurs under certain conditions. In this research, the aim is the suppression of internal defects, and final target is to create the optimal cold drawing conditions for pure magnesium wires. The first step is the investigation of the drawing limit by using 250°C annealed wire. As a result, reduction of 10% per pass was chosen for stable wire drawing. However, in this case, it was found that internal defects occurred at total reduction of over 45% during drawing. Investigation of intermediate annealing conditions that can suppress internal defects, and influence on internal defect that the die half angle and reduction per pass. As a result, it was found that the drawing condition capable of suppressing internal defects most efficiently was 13% reduction drawing by using under 6°half angle die. Consequently, it's possible to manufacture a cold fine drawn pure magnesium wire of 100?m, without defects in the center of the wire and hindering its mechanical properties.