Microdeformation in Heterogeneous Polymers, Revealed by Electron Microscopy

摘要

Recent investigations of the tensile fracture behaviour of representative glassy and semicrystalline impact-resistant polymers are reviewed, with emphasis on the microdeformation behaviour as revealed by electron microscopy of sections from bulk specimens, where the crack-tip damage zone has been embedded and/or stained under load, and on thin films deformed in situ. The insight that such techniques have provided into the toughening mechanisms is discussed.