Laser Alloying with WC Ceramic Powder in Hot Work Tool Steel using a High Power Diode Laser (HPDL)

摘要

Investigations include alloying the X38CrMoV5-3 hot-work tool steel surface layer with the tungsten carbide, using the high power diode laser (HPDL). The tungsten carbide ceramic particles of the medium grain size according to FSSS = 50μm were introduced using the rotor conveyer to improve the properties of the surface layer. The powder feed rate was set at the steady level of 8.64g/min. Remelting and alloying were carried out several times in the laser power range of 1.2 - 2.3 kW in the remelting/alloying, alloying/remelting sequences. The structural mechanism was determined of gradient layer development, effect was studied of alloying parameters, gas protection method, and powder feed rate on its mechanical properties, and especially on its hardness, abrasive wear resistance, and roughness. Structure changes were revealed consisting, in particular, in its refining, and also hardness and microhardness changes in comparizon to the nonremelted steel. Examination results obtained with the EDX microanalysis, surface and linear analysis of the chemical composition, as well as the X-ray qualitative phase analysis are presented.