INFLUNCE OF COOLING RATES ON NITROGEN PRECIPITATION BEHAVIORS AND THE FERRITE FRACTION IN CAST 2507 SUPER DUPLEX STAINLESS STEEL

摘要

2507 super duplex stainless steel (SDSS) has been widely applied in a marine environment, attributing to its excellent pitting corrosion resistance and mechanical properties which are particularly determined by the nitrogen precipitation behaviors and volume fraction of ferrite. In this paper, various cooling rates were obtained by applying four different moulds with the common gating system. By which the influence of cooling rates on nitrogen precipitation behaviors and the ferrite fraction in cast 2507 SDSS was comparatively investigated. The results showed that nitrogen porosity could easily precipitate in cast 2507 SDSS under standard atmospheric pressure. The number of nitrogen holes increased with decreasing the cooling rates, and the holes mainly distributed in three zones, i.e. the interface between the horizontal and vertical columnar grains, top vertical columnar grains and the final solidification region. Additionally, higher ferrite fraction was obtained with lower cooling rates.