MECHANICAL CHARACTERIZATION OF THE 3Y-TZP CO-DOPED WITH YTTRIA AND NIOBIA EQUIMOLAR ADDITION

摘要

The main goal of this work is to study the effect of the yttria and niobia equimolar addition in the 3Y-TZP on the mechanical properties (hardness, fracture toughness and four point bending strength) aiming to get a stable tetragonal phase (f) under applied stress, to use as TBC's. Four compositions with equimolar addition of yttria and niobia in the 3Y-TZP were produced, 13%, 14.5%, 16% and 17.5%. The mixtures were prepared in high energy ball milling for 10 minutes and the samples prepared on uniaxial and isostatic pressing. The selected temperature sintering was 1.550°C for 1 hour. Analyses of X-Ray Diffraction, hardness, fracture toughness and four point bending strength were performed. An increase on the mechanical properties analyzed was expected with yttria and niobia addition in comparision to 3Y-TZP, but instead a decrease was observed after these additions.