Microstructure Evolution of Copper by Three Roll Planetary Milling

摘要

The microstructure of commercial pure copper TP2 tube by three roll planetary mill processing was investigated. Due to work hardening and subsequent soiling by dynamic recrystallization during milling process, the coarse grain structure of the copper transformed to fine grain structure. The grain refinement is achieved along the axial moving in general; in the reducing zone, the sample has a gradient structure along the radial direction; uniform equiaxed grain with size of ～2 μm could be obtained at the outlet. The initiation of dynamic recrystallization occurred in the three roll planetary mill the reduction engineering strain reach ～30%, where some equiaxed grains replaced the elongated grains because of recrystallization.