Laser Powder Bed Fabrication of Nickel-Base Superalloys: Influence of Parameters; Characterisation, Quantification and Mitigation of Cracking

摘要

The use of a selective laser melting (SLM) powder-bed method to manufacture Ni-based superalloys components provides an economic approach for low production run components that operate under a high-temperature and stress environment. A major concern with the SLM of precipitation hardenable Ni-based superalloys is their high susceptibility to cracking, which has been heavily documented in the field of welding. Weld cracking may occur either during processing (hot cracking, liquation cracking and ductility-dip cracking) or during the post weld heat-treatment stage (strain-age cracking). Due to the complex thermal history of SLM fabricated material there is the potential for all of these mechanisms to be active.