Stress Corrosion Cracking and Corrosion Fatigue of Welded Joints of Some Al Alloys

机译：某些铝合金焊接接头的应力腐蚀开裂和腐蚀疲劳

获取原文

页面导航

摘要
著录项
相似文献
相关主题

摘要

The susceptibility of welded Johns of three aluminum alloy, two Al-Mg and one Al-Zn-Mg alloy to stress corrosion cracking and corrosion fatigue wa s investigated. The new Alustar Al-Mg alloy demostrated the best resistance to low cycle corrosion fatigue and intermediate resistance to stress corrosion cracking in sea water.

机译：研究了三种铝合金，两种铝镁合金和一种铝锌镁合金的焊接约翰斯合金对应力腐蚀开裂和腐蚀疲劳的敏感性。新型Alustar Al-Mg合金具有最好的抗低循环腐蚀疲劳性和中等抗海水应力腐蚀开裂的能力。

著录项

来源
《Fracture Mechanics Beyond 2000》|2002年|p.633-639|共7页
会议地点
作者
A. Zielinski; M. Czechowski; S. Rymkiewicz;
展开▼
作者单位

展开▼
会议组织
原文格式 PDF
正文语种
中图分类一般工业技术;
关键词

相似文献

外文文献
中文文献
专利

1. Stress corrosion cracking and fatigue crack growth of an API 5L X70 welded joint in an ethanol environment [J] . Giorgetti V, Santos E. A., Marcomini J. B., International Journal of Pressure Vessels and Piping . 2019,第期

机译：乙醇环境中API 5L X70焊接接头的应力腐蚀裂纹和疲劳裂纹生长
2. Effects of phosphorus segregation on stress corrosion cracking in the heat-affected zone of a dissimilar weld joint between a Ni-base alloy and a low alloy steel [J] . Ziqing Zhai, Hiroshi Abe, Yuichi Miyahara, Corrosion science . 2015,第mara期

机译：磷偏析对镍基合金与低合金钢异种焊接接头热影响区应力腐蚀开裂的影响
3. Role of water chemistry and microstructure in stress corrosion cracking in the fusion boundary region of an Alloy 182-A533B low alloy steel dissimilar weld joint in high temperature water [J] . Qunjia Peng, He Xue, Juan Hou, Corrosion science . 2011,第12期

机译：182-A533B低合金钢异种接头在高温水中的熔合边界区域中水化学和微观结构在应力腐蚀开裂中的作用
4. Stress Corrosion Cracking and Corrosion Fatigue of Welded Joints of Some Al Alloys [C] . A. Zielinski, M. Czechowski, S. Rymkiewicz Biennial Conference on Fracture . 2002

机译：一些AL合金焊接关节的应力腐蚀裂纹和腐蚀疲劳
5. Indications of Stress Corrosion Cracking Resistance in Alloy 82 Dissimilar Metal Welds in Simulated Primary Water Environments [D] . Persaud, Suraj 2011

机译：模拟的一次水环境中82合金异种金属焊缝的耐应力腐蚀开裂迹象
6. Stress Corrosion Cracking of Friction Stir-Welded AA-2024 T3 Alloy [O] . Marina Cabrini, Sara Bocchi, Gianluca D’Urso, 2020

机译：搅拌摩擦焊接AA-2024 T3合金的应力腐蚀开裂
7. Effects of alloy chemistry, cold work, and water chemistry on corrosion fatigue and stress corrosion cracking of nickel alloys and welds. [O] . Chopra, O. K., Soppet, W. K., Shack, W. J., 2001

机译：合金化学，冷加工和水化学对镍合金和焊缝腐蚀疲劳和应力腐蚀开裂的影响。
8. Corrosion Fatigue Crack Propagation in Aluminum Alloys. Part I. Effect of Cyclic Stress Wave Form on Corrosion Fatigue Crack Propagation in Al-Zn-Mg Alloys. Part II. Mechanisms of Corrosion Fatigue Crack Propagation in Al-Zn-Mg Alloys [R] . Selines, R. J., Stoltz, R. E., Pelloux, R. M. 1972

机译：铝合金腐蚀疲劳裂纹扩展。第一部分循环应力波形对al-Zn-mg合金腐蚀疲劳裂纹扩展的影响。第二部分。 al-Zn-mg合金腐蚀疲劳裂纹扩展机理

Stress Corrosion Cracking and Corrosion Fatigue of Welded Joints of Some Al Alloys

摘要

著录项

相似文献

相关主题

期刊订阅