The Influence of the Hot-Deformed State on the Recrystallization of Al-2.5Mg (AA5052)

摘要

A recent development of X-ray peak profile analysis has been used to evaluate the dislocation density (i.e. the stored energy) in five different texture components of a hot deformed aluminium-2.5wt%magnesium alloy (AA5052). These results have then been linked to EBSD data acquired on partially recrystalli-zed samples in order to clarify the relationships between grain orientation, stored energy and recrystallization behavior.