Fatigue Properties of Jute Fabric Reinforced Sheet Molding Compound (SMC) Molding

摘要

Recent earth environmental concern requires easy recycle material system, and the use of biodegradable polymer and natural fiber is noticed in composite materials. To apply the natural fiber for the structural parts, the use as reinforcement of Sheet Molding Compound (SMC) is desirable because it is expected that SMC can be used in various fields in terms of high productivity and dimensional stability.Considering that fiber reinforced composite is used for structural part, the design of the strength is very difficult because the failure mechanism is complicated considerably. In this study, SMC that reinforcement was jute cloth was prepared. The low-cycle bending fatigue test and the cross sectional observation of fracture part were performed. As a result, the brittle crack propagation in the interface around the fiber bundle was seen in the specimen of warp and weft direction, and the phenomenon such as brittle crack propagation was not confirmed in the specimen of 45-degree direction.