Superplastic Properties and Superplastic Forming/Diffusion Bonding of γ-TiAl+α_2-Ti3Al Sheet Materials

摘要

The as-cast and hot worked microstructures of the newly developed β-solidifying ingot-metallurgy Ti-45Al-X (Nb,Mo,B) alloy and its superplastic properties in the hot worked condition have been studied. The obtained experimental findings were used for research of superplastic forming and diffusion bonding of sheet products, which were cut out of hot worked preform by spark cutting. It was shown that superplastic forming might be successfully applied to the obtained fine-grained sheet materials. Relatively low bonding temperatures and pressures were found to be sufficient to achieve sound joints in the sheet material.