An Effect of High Magnetic Field on Grain Growth in Nanocrystalline Iron

摘要

A nanostructured surface layer on a pure iron sample was prepared by surface mechanical attrition treatment (SMAT). The thermal stability of SMAT sample was investigated at different temperatures with or without a high magnetic field (H =12T). It was found that a high magnetically annealing enhanced grain growth at the early stage of annealing, and produced a uniform nanocrystalline grain structure. After homogeneous grains developed, further grain growth became restrained.