Interface Properties of Copper/Aluminum/Stainless Steel Clad Materials

摘要

Copper/aluminum/stainless steel (Cu/Al/STS) clad materials were made by rolling and heat treatment process. These specimens were evaluated the formability and bonding strength of Cu/Al/STS clad materials. Thin disc specimens for TEM observation were prepared from the interfaces of Cu/Al and Al/STS by using the Focused Ion Beam (FIB) utility. Brittle oxide film formed on copper surface during heat treatment at 673K～773K. Diffusion bonding was observed at the interface of Cu/Al. Reacted region was formed in the interface of Al/STS with width about 10nm, while in the case of Cu/Al was formed about l,600nm width. It was also observed nano-sized crevice in reacted region of Al/STS interfaces.