Relationship between structure and dielectric properties of Bi-oriented isotactic polypropylene films for capacitors

摘要

This work reports on the relationship between structure and dielectric properties of biaxially oriented polypropylene. The morphology of semi-crystalline bioriented isotactic polypropylene (BOiPP) films is investigated using Wide Angle X-ray Diffraction (WAXD) and Polarized Optical Microscopy (POM). A β-orthorhombic structure, with a crystallinity ratio of about 46%, and a “Crater” morphology of the β-form is identified. Dielectric properties are measured by Broadband Dielectric Spectroscopy (BDS) over a wide temperature range (−150°C to 125°C). Since the dissipation factor of the PP is very low, special care was taken to obtain valid data. Two main relaxation processes are observed: a α-relaxation peak associated to the glass transition temperature (Tg) at low frequency and temperature about −7°C, and a broad β^∗-relaxation at high frequency at about −60°C, attributed to CH orientation. The variation of the dissipation factor versus sample thickness (from 3.8 μm to 11.8 μm) is correlated and explained by the increase of crystallinity ratio at larger thicknesses.