Design Method of Mix of Ready-Mixed Concrete to Manufacture Concrete Structures with Unit Weight of 2,700kg/m3 or More
展开▼
机译:现成混凝土混合制造混凝土结构的设计方法,单位重量为2,700kg / m3以上
展开▼
页面导航
摘要
著录项
相似文献
摘要
The present invention, 23 to 34% by weight of coarse aggregate consisting of steelmaking slag and having a unit specific gravity of 2.8 to 3.5t/m 3 to prevent damage or loss by external force according to climate change in the ocean; 23-41 wt% of fine aggregates having a unit specific gravity of 2.8-3.5t/m 3 and consisting of steelmaking slag; 10-15 wt% of a binder having a unit specific gravity of 2.6~2.7t/m 3 and consisting of loess powder; 15 to 18% by weight of mixed cement; 4-7% by weight of water; and 4 to 6% by weight of an AD admixture, the coarse aggregate is made of a particle size of 5 to 25 mm, the fine aggregate is made up of a particle size of 0.5 to 5 mm, and the ocher powder is 0.15 to 5 mm of It consists of a particle size, and the mixed cement is made by mixing Portland cement, blast furnace cement, and fly ash in a weight ratio of 5: 4: 1, and the AD admixture is an acrylic thickener 1 to 100 parts by weight of a cellulosic thickener. 10 parts by weight, 1 to 10 parts by weight of polyethylene oxide-based thickener, and 1 to 3 parts by weight of propylene carbonate are dissolved in water to liquefy and dried to form a powder thickener, water-reducing agent and crude polycarbonate-based fluidizing agent The crude polycarboxylic acid-based fluidizing agent comprises 50 to 70 parts by weight of tetraethoxysilane, 30 to 50 parts by weight of polyvinyl acetate, and trimethylolpropane triglycy based on 100 parts by weight of ethyl methacrylate. It is composed of 10 to 20 parts by weight of dilether and 5 to 15 parts by weight of polydimethylsiloxane, and the specific gravity is 2,700 kg/m 3 or more.
展开▼
机译:本发明,23至34重量%的粗骨料,由炼钢炉渣组成,单位比重为2.8至3.5t / m 3,以防止外部力损坏或根据海洋的气候变化; 23-41重量%的细骨料具有2.8-3.5t / m 3的单位比重,包括炼钢渣; 10-15重量%的粘合剂,单位比重为2.6〜2.7t / m 3,由黄土粉末组成; 15至18%重量的混合水泥; 4-7%的水;和4至6重量%的AD混合物,粗骨料由粒径为5至25mm,细聚集体由0.5至5mm的粒径组成,赭色粉末为0.15它的5毫米由粒径组成,并且混合水泥通过混合波特兰水泥,高炉水泥和粉煤灰以5:4:1的重量比混合制造,并且Ad混合物是丙烯酸增稠剂1至100零件重量的纤维素增稠剂。 10重量份,1至10重量份的聚环氧乙烷基增稠剂,1至3重量份的碳酸亚丙酯溶解在水中以液化并干燥,形成粉末增稠剂,减水剂和粗聚碳酸酯 - 基于流化剂的粗多元羧酸基流入剂包含50至70重量份的四乙氧基硅烷,30至50重量份的聚乙酸乙烯酯,基于100重量份的甲基丙烯酸乙酯,三羟甲基丙烷三丙酸盐。它由10至20重量份的稀释剂组成,5至15重量份的聚二甲基硅氧烷,比重为2,700kg / m 3以上。
展开▼