WROUGHT MAGNESIUM ALLOYS WITH HIGH MECHANICAL PROPERTIES AND METHOD FOR PREPARING THE SAME
WROUGHT MAGNESIUM ALLOYS WITH HIGH MECHANICAL PROPERTIES AND METHOD FOR PREPARING THE SAME
展开▼
机译:具有高机械性能的锻造镁合金及其制备方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
The present invention relates to bismuth (Bi) in an amount of 2.0 to 8.0% by weight; 0.5 to 6.5% by weight of aluminum (Al); Magnesium (Mg) balance; And it relates to a magnesium alloy extruded material containing unavoidable impurities, wherein the magnesium alloy extruded material according to the present invention further includes aluminum (Al) in the Mg-Bi binary alloy, thereby promoting dynamic recrystallization during extrusion to obtain uniform and fine grains. It has fine secondary phase (Mg 3 Bi 2 ) particles that are precipitated during extrusion together with the configured microstructure, and exhibits significantly improved strength and elongation compared to conventional magnesium extrusion materials without including rare earth metals.
展开▼
机译:本发明涉及2.0至8.0重量%的铋(Bi); 0.5至6.5%(重量)铝(Al); 镁(mg)平衡; 它涉及一种含有不可避免的杂质的镁合金挤出材料,其中根据本发明的镁合金挤出材料在Mg-Bi二元合金中还包括铝(Al),从而促进挤出过程中的动态重结晶,得到均匀和细粒 。 它具有在挤出过程中沉淀在挤出期间与配置的微观结构一起沉淀的细二相(Mg 3 Bi 2)颗粒,与常规的镁挤出材料相比,表现出显着提高的强度和伸长率,而不包括稀土金属。
展开▼