STYROLHARZ, STYROLHARZZUM SUMMARY, DARAUS FORMARTICS AND STYROLHARZMANUFACTURING PROCEDURES
STYROLHARZ, STYROLHARZZUM SUMMARY, DARAUS FORMARTICS AND STYROLHARZMANUFACTURING PROCEDURES
展开▼
机译:苯乙烯树脂,苯乙烯树脂血液综述,其中格式和搅拌器哈尔兹曼制造程序
展开▼
页面导航
摘要
著录项
相似文献
摘要
To provide a styrene resin having a syndiotactic structure, which has a proportion of an endothermic amount obtained in a range of 175 to 260°C of less than 30% based on the total endothermic amount taken as 100%, which are measured at a temperature rise rate of 20°C/min through differential scanning calorimetry, and a styrene resin composition containing 50 to 95% by mass of a thermoplastic resin composition and 5 to 50% by mass of a glass filler, the thermoplastic resin composition containing 100 parts by mass of a thermoplastic resin (SCA) containing 80 to 100% by mass of a styrene resin having a syndiotactic structure and 0 to 20% by mass of a rubbery elastic material, 0.2 to 2.0 parts by mass of at least one kind of an antioxidant (SCB) selected from the group consisting of a phenol-based antioxidant and a sulfur antioxidant, 1.5 to 5.0 parts by mass of at least one kind of a compound (SCC) selected from the group consisting of a polyphenylene ether and a modified polyphenylene ether, and at least one kind selected from the group consisting of a nucleating agent and a release agent.
展开▼
机译:提供具有间同立构结构的苯乙烯树脂,其在175至260℃的范围内具有小于30%的聚比例,其基于作为100%的总吸热量,其在温度下测量通过差示扫描量热法,20℃/ min的上升速率,以及含有50至95质量%的热塑性树脂组合物和5至50质量%的玻璃填料,含有100份的热塑性树脂组合物的苯乙烯树脂组合物。热塑性树脂的质量(Sc a sup>)含有80-100质量%的苯乙烯树脂,其具有间同立构结构和0至20质量%的橡胶状弹性材料,0.2至2.0质量份至少一种选自酚类抗氧化剂和硫抗氧化剂的抗氧化剂(SC B / SOP>),其至少一种化合物的硫抗氧化剂和硫抗氧化剂,1.5至5.0质量份( Sc c sup>选自聚苯醚R和改性的聚苯醚,以及选自成核剂和脱模剂的至少一种。
展开▼