FILM-FORMING COMPOSITION, METHOD FOR PRODUCING SURFACE-TREATED METAL MEMBER, AND METHOD FOR PRODUCING METAL-RESIN COMPOSITE
FILM-FORMING COMPOSITION, METHOD FOR PRODUCING SURFACE-TREATED METAL MEMBER, AND METHOD FOR PRODUCING METAL-RESIN COMPOSITE
展开▼
机译:成膜组合物,制备表面处理的金属构件的方法,以及生产金属 - 树脂复合材料的方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
Provided are a film-forming composition for forming a film having excellent adhesion to a resin on a metal surface, and a surface-treated metal member comprising a film formed using the composition. The composition for film formation is a solution containing the silane coupling agent containing an amino group, a metal ion, and a halide ion. The metal ion is preferably a copper ion, and the copper ion concentration in the solution is preferably 0.1 to 60 mM. As for the quantity of Si with respect to the quantity of Cu in a solution, 30 or less are preferable in molar ratio. The pH of the solution is preferably 2.8 to 6.2.